(Summary description)WeituoWeituoFluidEquipmentWATOWuhanWeituoFluidControlEquipmentCo.,Ltd.Valveisacontrolcomponentinafluidconveyingsystem.Ithasthefunctionsofcut-off,regulation,diversion,preventionofreverseflow,stabilization,diversionoroverflowandpressurerelief.Valvesusedinfluidcontrolsystems,rangingfromthesimplestshut-offvalvestothevariousvalvesusedinextremelycomplexautomaticcontrolsystems,haveawiderangeofvarietiesandspecifications.Thecorrosionofthevalveisusuallyunderstoodasthedamagetothemetalmaterialofthevalveundertheactionofachemicalorelectrochemicalenvironment.Sincethe"corrosion"phenomenonoccursinthespontaneousinteractionbetweenthemetalandthesurroundingenvironment,howtoisolatethemetalfromthesurroundingenvironmentorusemorenon-metallicsyntheticmaterialsisthefocusofcorrosionprevention.Thevalvebodyincludesthevalvecover,whichoccupiesmostoftheweightofthevalveandisinconstantcontactwiththemedium.Therefore,theselectionofthevalveisoftenbasedonthevalvebodymaterial.Theanti-corrosionofthevalvebodyismainlybasedonthecorrectselectionofmaterials.Althoughthereareabundantanti-corrosionmaterials,itisnoteasytochoosetherightone,becausetheproblemofcorrosionisverycomplicated.Forexample,sulfuricacidisverycorrosivetosteelwhentheconcentrationislow,andwhentheconcentrationishigh,thesteelisproduced.Passivationfilmcanpreventcorrosion;hydrogenonlyshowsstrongcorrosivenesstosteelunderhightemperatureandhighpressure.Whenchlorineisinadrystate,thecorrosionperformanceisnotgreat,butwhenthereisacertainhumidity,thecorrosionperformanceisverystrong,andmanymaterialscannotbeused..Thedifficultyinselectingvalvebodymaterialsliesinnotonlyconsideringcorrosionissues,butalsofactorssuchaspressureresistanceandtemperatureresistance,whetheritiseconomicallyreasonable,andwhetheritiseasytopurchase.Soitmustbeattentive.Therearetwoformsofcorrosionofthevalvebody,namelychemicalcorrosionandelectrochemicalcorrosion.Itscorrosionratedependsonthetemperature,pressure,chemicalpropertiesofthemediumandthecorrosionresistanceofthevalvebodymaterial.Thecorrosionratecanbedividedintosixlevels:1.Completecorrosionresistance:thecorrosionrateislessthan0.001mm/year;2.Extremelyresistanttocorrosion:thecorrosionrateis0.001to0.01mm/year;3,corrosionresistance:corrosionrate0.01to0.1mm/year;4.Stillcorrosionresistant:thecorrosionrateis0.1to1.0mm/year;5.Poorcorrosionresistance:thecorrosionrateis1.0to10mm/year;6.Notcorrosionresistant:thecorrosionrateisgreaterthan10mm/year.Thesecondistotakeliningmeasures,suchaslininglead,liningaluminum,liningengineeringplastics,liningnaturalrubberandvarioussyntheticrubbers.Ifthemediaconditionspermit,thisisaneconomicalmethod.Furthermore,inthecaseoflowpressureandtemperature,usingnon-metalasthevalvebodymaterialcanoftenbeveryeffectiveinpreventingcorrosion.Theoutersurfaceofthevalvebodyisalsocorrodedbytheatmosphere,andgenerallysteelmaterialsareprotectedbypainting.
Introduction to the protection of valve corrosion
(Summary description)WeituoWeituoFluidEquipmentWATOWuhanWeituoFluidControlEquipmentCo.,Ltd.Valveisacontrolcomponentinafluidconveyingsystem.Ithasthefunctionsofcut-off,regulation,diversion,preventionofreverseflow,stabilization,diversionoroverflowandpressurerelief.Valvesusedinfluidcontrolsystems,rangingfromthesimplestshut-offvalvestothevariousvalvesusedinextremelycomplexautomaticcontrolsystems,haveawiderangeofvarietiesandspecifications.Thecorrosionofthevalveisusuallyunderstoodasthedamagetothemetalmaterialofthevalveundertheactionofachemicalorelectrochemicalenvironment.Sincethe"corrosion"phenomenonoccursinthespontaneousinteractionbetweenthemetalandthesurroundingenvironment,howtoisolatethemetalfromthesurroundingenvironmentorusemorenon-metallicsyntheticmaterialsisthefocusofcorrosionprevention.Thevalvebodyincludesthevalvecover,whichoccupiesmostoftheweightofthevalveandisinconstantcontactwiththemedium.Therefore,theselectionofthevalveisoftenbasedonthevalvebodymaterial.Theanti-corrosionofthevalvebodyismainlybasedonthecorrectselectionofmaterials.Althoughthereareabundantanti-corrosionmaterials,itisnoteasytochoosetherightone,becausetheproblemofcorrosionisverycomplicated.Forexample,sulfuricacidisverycorrosivetosteelwhentheconcentrationislow,andwhentheconcentrationishigh,thesteelisproduced.Passivationfilmcanpreventcorrosion;hydrogenonlyshowsstrongcorrosivenesstosteelunderhightemperatureandhighpressure.Whenchlorineisinadrystate,thecorrosionperformanceisnotgreat,butwhenthereisacertainhumidity,thecorrosionperformanceisverystrong,andmanymaterialscannotbeused..Thedifficultyinselectingvalvebodymaterialsliesinnotonlyconsideringcorrosionissues,butalsofactorssuchaspressureresistanceandtemperatureresistance,whetheritiseconomicallyreasonable,andwhetheritiseasytopurchase.Soitmustbeattentive.Therearetwoformsofcorrosionofthevalvebody,namelychemicalcorrosionandelectrochemicalcorrosion.Itscorrosionratedependsonthetemperature,pressure,chemicalpropertiesofthemediumandthecorrosionresistanceofthevalvebodymaterial.Thecorrosionratecanbedividedintosixlevels:1.Completecorrosionresistance:thecorrosionrateislessthan0.001mm/year;2.Extremelyresistanttocorrosion:thecorrosionrateis0.001to0.01mm/year;3,corrosionresistance:corrosionrate0.01to0.1mm/year;4.Stillcorrosionresistant:thecorrosionrateis0.1to1.0mm/year;5.Poorcorrosionresistance:thecorrosionrateis1.0to10mm/year;6.Notcorrosionresistant:thecorrosionrateisgreaterthan10mm/year.Thesecondistotakeliningmeasures,suchaslininglead,liningaluminum,liningengineeringplastics,liningnaturalrubberandvarioussyntheticrubbers.Ifthemediaconditionspermit,thisisaneconomicalmethod.Furthermore,inthecaseoflowpressureandtemperature,usingnon-metalasthevalvebodymaterialcanoftenbeveryeffectiveinpreventingcorrosion.Theoutersurfaceofthevalvebodyisalsocorrodedbytheatmosphere,andgenerallysteelmaterialsareprotectedbypainting.
- Categories:Trade News
- Author:WATO
- Origin:Wuhan Weituo Fluid Control Equipment Co., Ltd.
- Time of issue:2018-10-30
- Views:92
Weituo Weituo Fluid Equipment WATO Wuhan Weituo Fluid Control Equipment Co., Ltd.
Valve is a control component in a fluid conveying system. It has the functions of cut-off, regulation, diversion, prevention of reverse flow, stabilization, diversion or overflow and pressure relief. Valves used in fluid control systems, ranging from the simplest shut-off valves to the various valves used in extremely complex automatic control systems, have a wide range of varieties and specifications.
The corrosion of the valve is usually understood as the damage to the metal material of the valve under the action of a chemical or electrochemical environment. Since the "corrosion" phenomenon occurs in the spontaneous interaction between the metal and the surrounding environment, how to isolate the metal from the surrounding environment or use more non-metallic synthetic materials is the focus of corrosion prevention.
The valve body includes the valve cover, which occupies most of the weight of the valve and is in constant contact with the medium. Therefore, the selection of the valve is often based on the valve body material. The anti-corrosion of the valve body is mainly based on the correct selection of materials. Although there are abundant anti-corrosion materials, it is not easy to choose the right one, because the problem of corrosion is very complicated. For example, sulfuric acid is very corrosive to steel when the concentration is low, and when the concentration is high, the steel is produced. Passivation film can prevent corrosion; hydrogen only shows strong corrosiveness to steel under high temperature and high pressure. When chlorine is in a dry state, the corrosion performance is not great, but when there is a certain humidity, the corrosion performance is very strong, and many materials cannot be used. . The difficulty in selecting valve body materials lies in not only considering corrosion issues, but also factors such as pressure resistance and temperature resistance, whether it is economically reasonable, and whether it is easy to purchase. So it must be attentive.
There are two forms of corrosion of the valve body, namely chemical corrosion and electrochemical corrosion. Its corrosion rate depends on the temperature, pressure, chemical properties of the medium and the corrosion resistance of the valve body material. The corrosion rate can be divided into six levels:
1. Complete corrosion resistance: the corrosion rate is less than 0.001 mm/year;
2. Extremely resistant to corrosion: the corrosion rate is 0.001 to 0.01 mm/year;
3, corrosion resistance: corrosion rate 0.01 to 0.1 mm/year;
4. Still corrosion resistant: the corrosion rate is 0.1 to 1.0 mm/year;
5. Poor corrosion resistance: the corrosion rate is 1.0 to 10 mm/year;
6. Not corrosion resistant: the corrosion rate is greater than 10 mm/year.
The second is to take lining measures, such as lining lead, lining aluminum, lining engineering plastics, lining natural rubber and various synthetic rubbers. If the media conditions permit, this is an economical method. Furthermore, in the case of low pressure and temperature, using non-metal as the valve body material can often be very effective in preventing corrosion. The outer surface of the valve body is also corroded by the atmosphere, and generally steel materials are protected by painting.
Scan the QR code to read on your phone
Wuhan Weituo Fluid Control Equipment Co., Ltd
Address: Room 1706, Building D, Wuhan Living Room, No.8 Hongtu Avenue, Dongxihu District, Wuhan City
Tel:0086-18942929031 0086-027-83612831
Fax:0086-027-83612830
E-mail:wato@163.com
Address:www.watoer.com www.watovale.cn 伟拓.网址


Mobile web site
Copyright © 2020 Wuhan Weituo Fluid Control Equipment Co., Ltd 鄂ICP备19156067号 Powered by:300.cn